Features:
Combine Part A (resin) and
Part B (hardener) in the correct ratio,
and mix thoroughly until the color and
consistency are uniform.
Classify:
1. Room
temperature cure Epoxy: Complete cure is
obtained after 24 hours at room
temperature after mixing.
2. Heat cure Epoxy: Heat after mixing to
shorten the curing time.
3. Single component heat cure Epoxy:
Single component, reaction will occur
after heating
|
|
Click on the "grades" you are interested in, they will be added to the inquiry list
automatically.. (Click here to send out the inquiry. )
|
Grade |
Color
|
Mixing
Ration(Weight) |
Viscosity
CPS |
Using
time @25℃ |
Harden
time @25℃ |
Rigidity
(shore) |
Feature |
|
AB3100T |
A:Transparence
B:Transparence |
3:1 |
A:7500
B:100 |
20
mins. |
6~10
hrs |
D80~85 |
Low viscosity, fluidity, transparent and hard, gloss, flat and low shrink after cured, excellent insulation. Ideal for electronic parts and
craftwork potting, can be modified to different color. |
|
AB3800T |
A:Transparence
B:Transparence |
3:1 |
A:7500
B:500 |
20
mins. |
6~10
hrs |
D30~40 |
Low viscosity and fluidity, transparent, flexible, gloss flat and low shrink
after cured, excellent insulation. Ideal for electronic parts and craftwork potting, can be modified to different color. |
|
EX2100 |
A:Black
B:Brown |
2:1 |
A:10000
B:400 |
40
mins. |
6~8
hrs |
D80~85 |
Medium viscosity, gloss and hard after cured. Ideal for transformer and
electronic devices potting. |
|
EX4100 |
A:Black
B:Brown |
4:1 |
A:1500
B:150 |
40
mins. |
6~10
hrs |
D80~85 |
Low viscosity, fluidity, hard and gloss, flat surface after cured, excellent
insulator. Ideal for transformer and electronic devices potting and can be modified to different color. |
|
EX5100 |
A:Black
B:Brown |
5:1 |
A:1600
B:50 |
40
mins. |
6~10
hrs |
D80~85 |
Low viscosity, fluidity, gloss and flat surface, hard after cured, excellent
insulation. Ideal for transformer and electronic devices potting and can be modified to different color. |
|
G-8500 |
A:Black
B:Brown |
4:1 |
A:1700
B:250 |
40
mins. |
6~10
hrs |
D80~85 |
Passed UL standard, two component
EPOXY. |
|
|
|